PVDF/TiO2 nanocomposites prepared by solution blow spinning: surface properties and their relation with S. Mutans adhesion

Loading...
Thumbnail Image
Identifiers
Publication date
2017-04
Defense date
Advisors
Tutors
Journal Title
Journal ISSN
Volume Title
Publisher
Elsevier
Impact
Google Scholar
Export
Research Projects
Organizational Units
Journal Issue
Abstract
Thermoplastic nanocomposite materials with potential bactericide properties were prepared and their surface properties and adhesion to Streptococcus mutans, S. mutans, were characterized. Solution blow spinning was successfully used to prepare films with a fiber-like structure on the surface of nanocomposites based on Polyvinylidene fluoride, PVDF, filled with well dispersed TiO2 nanoparticles. PVDF/TiO2 nanocomposites were prepared varying the nanoparticles content (0%, 1%, 2%, 5% and 10% by weight). In order to understand the influence of the presence of TiO2 nanoparticles and the final surface properties on the adhesion of S. mutans to the materials, a deep characterization was carried out focusing on the morphology, roughness, surface free energy from contact angle measurements and cell adhesion by single cell force spectroscopy. It was observed that the uniform dispersion of the nanofiller arose from nanoparticles embedded in the polymer when fibers were created during the blow spinning process. TiO2 content influenced the topography of the films probably due to a direct effect on the solvent evaporation rate. Although this factor greatly conditioned the roughness of the samples and therefore the surface free energy, S. mutant adhesion on the substrates under study was concluded to be more dependent on the specific interactions with the surface polar groups of the material.
Description
Keywords
PVDF, TiO2, Blow spinning, Nanocomposites, Cell adhesion
Bibliographic citation
González-Benito, J., Teno, J., González-Gaitano, G., Xu, S. & Chiang, M. (2017). PVDF/TiO2 nanocomposites prepared by solution blow spinning: Surface properties and their relation with S. Mutans adhesion. Polymer Testing, vol. 58, pp. 21–30.