Publication: Influence of vacuum hot-pressing temperature on the microstructure and mechanical properties of Ti—2.5V alloy obtained by blended elemental and master alloy addition powders
Loading...
Identifiers
Publication date
2012-12
Defense date
Advisors
Tutors
Journal Title
Journal ISSN
Volume Title
Publisher
Elsevier
Impact
Export
Abstract
This study addresses the processing of near-net-shape, chemically homogeneous and fine-grained Ti–3Al–2.5V components using vacuum hot-pressing. Two Ti–3Al–2.5V starting powders were considered. On one side, hydride-dehydride (HDH) elemental titanium was blended with an HDH Ti–6Al–4V prealloyed powder. On the other side, an Al:V master alloy was added to the HDH elemental titanium powder. The powders were processed applying a uniaxial pressure of 30 MPa. The sintering temperatures studied varied between 900 degrees C and 1300 degrees C. The relative density of the samples increased with processing temperature and almost fully dense materials were obtained. The increase of the sintering temperature led also to a strong reaction between the titanium powders and the processing tools. This phenomenon occurred particularly with boron nitride (BN) coating, which was used to prevent the direct contact between titanium and graphite tools. The flexural properties of the Ti–3Al–2.5V samples increased with vacuum hot-pressing temperature and are comparable to those specified for wrought titanium medical devices. Therefore, the produced materials are promising candidates for load bearing applications as implant materials.
Description
Keywords
Prealloyed, Master alloy, Vacuum hot-pressing, Mechanical properties, Ti—3Al—2.5V, BN—Ti interaction
Bibliographic citation
Materials Chemistry and Physics (2012). 137(2), 608-616.