Dios Pérez, Miguel deGonzález, Z.Alvaredo Olmos, PaulaBermejo, RaúlGordo Odériz, ElenaFerrari, Begoña2018-04-162019-11-152017-11-15Journal of Alloys and Compounds, 724, (Nov. 2017), 327-338.0925-8388https://hdl.handle.net/10016/26650In this work, the combination of colloidal and powder metallurgy techniques was proposed as an alternative route to produce Ti(C,N)-based cermets with a 15-20 vol% of Fe/Ni alloy (85/15 wt%) as metal matrix. The novelty of this processing route is based in the mixture of fine powders (1;-3 µm) in suspension which promotes the uniformity of the phase distribution and consequently its reactivity, leading to 99.9% dense cermets with 1300 Vickers Hardness (HV30). The preparation of colloidal and chemically stable slurries of non-oxide and metal powders in aqueous media is a key step of the process. Highly concentrated aqueous slurries of Ti(C,N), Fe, Ni and C powders were prepared and mixed. Then bulk pieces were shaped by Slip casting (SC), Slip Casting + Cold Isostatic Pressing (SC-CIP) and Spray-Dry + Uniaxial Pressing of the obtained spherical granules (SDP). The composite formulation and the thermal treatment were optimized to prevent Ni sublimation during sintering as well as to improve liquid phase sintering in terms of wetting and reactivity among well packed particles. The effective dispersion of the slurry and the synergistic effect of combined techniques yielded the preparation of reliable materials by the SDP process with 15 wt% of FeNi with the addition of 0.5 wt% of C. The optimization of the composite formulation and the processing parameters improves both density and hardness of a finer microstructure of the composite after a short sintering treatment (120 min) at 1450 °C in vacuum.11application/pdfeng© 2017 Elsevier B.V. All rights reservedColloidal processingPowder metallurgical processingTi(C,N)-based cermetsFe/NiHardnessresearch articleMaterialeshttps://doi.org/10.1016/j.jallcom.2017.07.034open access327338Journal of Alloys and Compounds724AR/0000021107