Improvement of high temperature oxidation resistance of γTiAl alloys by slurry coatings

Repositorio e-Archivo

Mostrar el registro sencillo del ítem

dc.contributor.advisor Ruiz Navas, Elisa Mª
dc.contributor.advisor Tsipas, Sophia Alexandra
dc.contributor.author Musallam, Nicolás Fashho
dc.date.accessioned 2016-04-05T18:45:42Z
dc.date.available 2016-04-05T18:45:42Z
dc.date.issued 2014
dc.date.submitted 2014-07-14
dc.identifier.uri http://hdl.handle.net/10016/22665
dc.description.abstract This research document aims to deepen the understanding of slurry coatings as an effective barrier against the oxidation of promising Titanium-aluminide intermetallic alloys. For that purpose, the research is carried out with a Titanium- Aluminum alloy substrate {(Ti 45Al 2Nb 2Mn + 0.8%vol TiB2){ which was manufactured by means of two different techniques: Hot Isostatic Pressing (HIP) and Centrifugal Casting (CC). Additionally, two different slurry coatings have been applied and analyzed in order to understand the effects they produce. One of them was based on Aluminum powders and the other on a mixture of Aluminum-Boron powders. Both carry polyethylene glycol (PEG) as a binder. A total of twenty four samples were used, from which twelve were manufactured by hot isostatic pressing and the remaining twelve by centrifugal casting. Each group of twelve pieces was divided in three subgroups, each made up of four samples. The first subgroup was subjected to oxidation without having any coating, the second was coated by the aluminum slurry and the third by the aluminum-boron slurry. The samples were oxidized in static air for 300 hours at 800ºC (1073 K) in an interrupted oxidation test. Finally, the characterization of the samples was performed by means of massgain, X-Ray diffraction and Scanning Electron Microscope (SEM) analyses.
dc.format.mimetype application/pdf
dc.language.iso eng
dc.rights Atribución-NoComercial-SinDerivadas 3.0 España
dc.rights.uri http://creativecommons.org/licenses/by-nc-nd/3.0/es/
dc.subject.other Oxidación
dc.subject.other Aleaciones
dc.subject.other Metales
dc.subject.other Materiales de recubrimiento
dc.subject.other Ensayo de materiales
dc.subject.other Titanio
dc.title Improvement of high temperature oxidation resistance of γTiAl alloys by slurry coatings
dc.type bachelorThesis
dc.subject.eciencia Aeronáutica
dc.rights.accessRights openAccess
dc.description.degree Ingeniería Aeroespacial
dc.contributor.departamento Universidad Carlos III de Madrid. Departamento de Ciencia e Ingeniería de Materiales e Ingeniería Química
 Find Full text

Ficheros en el ítem

*Click en la imagen del fichero para previsualizar.(Los elementos embargados carecen de esta funcionalidad)


El ítem tiene asociada la siguiente licencia:

Este ítem aparece en la(s) siguiente(s) colección(es)

Mostrar el registro sencillo del ítem