Estudio del efecto halógeno en la oxidación de aleaciones Ti-Al-V

e-Archivo Repository

Show simple item record

dc.contributor.advisor Tsipas, Sophia Alexandra
dc.contributor.author Sánchez del Cojo, Luis
dc.date.accessioned 2011-07-07T16:48:29Z
dc.date.available 2011-07-07T16:48:29Z
dc.date.issued 2011-04
dc.date.submitted 2011-04-29
dc.identifier.uri http://hdl.handle.net/10016/11719
dc.description.abstract El titanio y sus aleaciones tienen muy buenas propiedades, pero éstas se deterioran notablemente en aplicaciones de alta temperatura en las que se oxidan fácilmente. Se ha comprobado que pequeñas cantidades de elementos halógenos introducidos en la superficie de aleaciones intermetálicas de Ti-Al causan una importante mejora de las propiedades frente a la oxidación a altas temperaturas de estas aleaciones. Este efecto, conocido como efecto halógeno, no ha sido observado en aleaciones de Ti-Al-V. En este proyecto se pretende estudiar el efecto halógeno en muestras pulvimetalúrgicas y laminadas de la aleación Ti-6Al-4V, con el objetivo de encontrar una mejoría en el comportamiento a oxidación a alta temperatura. Las muestras pulvimetalúrgicas con las que se trabajó fueron fabricadas en el laboratorio a partir de polvos de aleación. El tratamiento de halogenación se realizó mediante la inmersión de las muestras en una mezcla polvos con un contenido de un 3% en peso de NH4Cl, a las temperaturas de 200°C, 600°C y 950°C. La resistencia a oxidación a alta temperatura de todas las muestras se evaluó mediante un tratamiento de oxidación a 600°C durante 300 horas. Finalmente, las muestras se analizaron mediante técnicas de difracción de Rayos – X y mediante análisis microestructural de secciones transversales, utilizando para ello un microscopio electrónico de barrido, MEB. ___________________________________________________________________________________________________________
dc.description.abstract Titanium and titanium alloys have very good properties, however they exhibit low oxidation resistance when exposed to high temperatures. It has been observed that when small quantities of a halogen element are implanted into the surface of Ti-Al intermetallic alloys their oxidation properties at high temperatures substantially improve. This effect, known as the halogen effect, has not been observed in Ti-Al-V alloys. This project aims to study the halogen effect in powder metallurgy and laminated samples of the Ti-6Al-4V alloy, in order to improve oxidation behavior at high temperature oxidation. The powder metallurgy samples used were manufactured in the laboratory from alloy powders. Halogenation treatment was performed by immersing samples in a powder mixture containing 3% wt of NH4Cl, at temperatures of 200 ° C, 600 ° C and 950 ° C. High temperature oxidation resistance of all samples was assessed by an oxidation treatment at 600 ° C for 300 hours. Finally, samples were studied by X Ray Diffraction and by the microstructural analysis of cross sections, using a scanning electron microscope, SEM.
dc.format.mimetype application/pdf
dc.language.iso spa
dc.rights Atribución-NoComercial-SinDerivadas 3.0 España
dc.rights.uri http://creativecommons.org/licenses/by-nc-nd/3.0/es/
dc.subject.other Oxidación
dc.subject.other Aleaciones metálicas
dc.subject.other Efecto halógeno
dc.subject.other Pulvimetalurgia
dc.title Estudio del efecto halógeno en la oxidación de aleaciones Ti-Al-V
dc.type masterThesis
dc.subject.eciencia Materiales
dc.rights.accessRights openAccess
dc.description.degree Ingeniería Industrial
dc.contributor.departamento Universidad Carlos III de Madrid. Departamento de Ciencia e Ingeniería de Materiales e Ingeniería Química
 Find Full text

Files in this item

*Click on file's image for preview. (Embargoed files's preview is not supported)


The following license files are associated with this item:

This item appears in the following Collection(s)

Show simple item record